Thông tin tài liệu
Thông tin siêu dữ liệu biểu ghi
| Trường DC | Giá trị | Ngôn ngữ |
|---|---|---|
| dc.contributor.author | Tabata, Chihiro | - |
| dc.contributor.author | Osada, Toshio | - |
| dc.contributor.author | Yokokawa, Tadaharu | - |
| dc.date.accessioned | 2023-10-06T07:11:07Z | - |
| dc.date.available | 2023-10-06T07:11:07Z | - |
| dc.date.issued | 2023 | - |
| dc.identifier.uri | https://link.springer.com/article/10.1007/s11661-023-07205-7 | - |
| dc.identifier.uri | https://dlib.phenikaa-uni.edu.vn/handle/PNK/9491 | - |
| dc.description | CC-BY | vi |
| dc.description.abstract | To clarify the effect of solution heat-treatment on the oxidation resistance of Ni-base single-crystal superalloy TMS-238, the evaluation of dendrite/inter-dendrite segregation of alloying elements in the as-cast and heat-treated samples, and its effect on cyclic oxidation resistance were investigated. Cyclic oxidation test results at 1100 °C for up to 150 cycles clearly showed that the as-cast samples with element segregations had lower oxidation resistance compared to heat-treated samples with homogeneous structure. Further, for the as-cast sample, rapid growth and spallation of oxide consisting of NiO, Cr2O3, and Al2O3 were observed around the dendrite core for 10 cycles of oxidation. | vi |
| dc.language.iso | en | vi |
| dc.publisher | Springer | vi |
| dc.subject | Solution Heat-Treatment | vi |
| dc.subject | Ni-Base Single-Crystal Superalloy | vi |
| dc.title | Effect of Solution Heat-Treatment on the Oxidation Resistance of Ni-Base Single-Crystal Superalloy | vi |