Effect of die coating on surface crack depth of hot extruded 7075 aluminum alloy

Abstract

The aluminum alloys belonging to the 7000 series are high-strength alloys used in a wide variety of products for weight reduction. They are primarily used in the field of transportation and aerospace. Among these, the A7075 alloy has the highest strength and is expected to be applicable in a wide range of fields, such as aircraft components and sports equipment. However, it has high deformation resistance and is prone to surface defects, which is called tearing. Tearing typically occurs at high temperatures and high ram speeds, and adversely affects productivity. The localized melting of Zn and additive compounds, due to the heat generated during the process, is considered to cause tearing. In this study, the effect of friction, heat, and tearing at the tool—metal interface was mitigated by improving the die surface quality.