Temperature stability of Co/Pt and Co/Pd synthetic antiferromagnets using an Ir spacer |
Tác giả : |
Caseiro, M. Macedo, R. Araujo, P. D. R. |
Năm xuất bản : |
2023 |
Nhà xuất bản : |
Springer |
Tóm tắt : |
The magnetic properties of Co/Pt and Co/Pd multilayers of perpendicular synthetic antiferromagnets with an Ir spacer were investigated. A strong interlayer exchange coupling of Jex=2.01 erg/cm2 was observed in the Co/Pt-based structures and a lower value of Jex=1.04 erg/cm2 was found in the Co/Pd multilayers. Only the former revealed a high post-annealing stability at Ta=330∘ C, as the latter exhibited a ferromagnetic coupling most likely due to the deterioration of the spacer by pinhole coupling. This assumption was confirmed by theoretical calculations of the total energy functional. Moreover, the high temperature stability of Ir-based Co/Pt p-SAF structures was verified by calculating the exchange field Hex from magnetization M(H) loops as a function of temperature, where it reached a temperature of Tb=370∘ C before losing all interlayer exchange coupling. Magnetic tunnel junctions (p-MTJs) with p |
Mô tả: |
CC-BY |
URI: |
https://link.springer.com/article/10.1007/s10854-023-11053-x https://dlib.phenikaa-uni.edu.vn/handle/PNK/8943 |
Bộ sưu tập |
OER - Khoa học Vật liệu, Ứng dụng |
XEM MÔ TẢ
13
XEM TOÀN VĂN
6
Danh sách tệp tin đính kèm: