Electrical transport properties of YBa2Cu3Oy implanted by CdS nanoparticles nanoparticle size effect |
Tác giả : |
Hkiri, Khaoula Mohamed, Hamza Elsayed Ahmed Shahzad, Nimra |
Năm xuất bản : |
2023 |
Nhà xuất bản : |
Springer |
Tóm tắt : |
Cadmium sulfide nanoparticles size effects on the superconducting properties of YBa2Cu3Oy compound were investigated in details. Solid-state reaction method was used for the synthesis of samples with additional amounts of CdS nanoparticles with sizes 6 nm and 12 nm and an additional amount x = 0.1 wt%. Synthesis of cadmium nanoparticles was done by using aqueous methods and they were characterized by using transmission electron microscopy (TEM), X-ray diffraction (XRD). Optical absorption measurement of the as-synthesized nanoparticles was carried out, and the specific surface areas of the sample were analyzed using a surface area and porosity analyzer. Electrical resistivity and transport critical current densities were measured by using the four-probe technique. The measurements revealed that CdS (6 nm) added samples exhibit higher energy pinning and current densities as compared to pure YBa2Cu3Oy and with additional CdS (12 nm). |
Mô tả: |
CC-BY |
URI: |
https://link.springer.com/article/10.1007/s10854-023-11170-7 https://dlib.phenikaa-uni.edu.vn/handle/PNK/8994 |
Bộ sưu tập |
OER - Khoa học Vật liệu, Ứng dụng |
XEM MÔ TẢ
15
XEM TOÀN VĂN
6
Danh sách tệp tin đính kèm: